A286 Stainless Steel Bar

A286 Bar

Description

A286 is a precipitation hardenable alloy. High Nickel and Chromium content gives it a good resistance to Corrosion up to about 1300 Deg C and Oxidation up to about 1500 Deg F. A286 can be age hardened to a high strength level. The alloy is also used for low temperature applications requiring a ductile, non-magnetic high strength material at temperatures ranging from above room temperature down to at least -320 Deg F. The alloy may be used for moderate corrosion applications in aqueous solutions.

Specific Gravity

7.9 g/cm3

Typical Applications

Related Specifications

Fasteners

Stud Bolts

Industrial Gas Turbines

AMS 5726

AMS 5731

AMS 5732

AMS 5737

BS HR 51

BS HR 52

W.Nr 1.4943

W.Nr 1.4944

UNS S66286

Chemical Composition (Wt %)

  C Mn P S Si Cr Ni Mo Ti V Al B Fe
Min  - - - - - 13.5 24 1 1.9 0.10 - 0.003 -
Max 0.08 2.0 0.025 0.025 1 16 27 1.5 2.35 0.50 0.035 0.010 Bal

Typical Mechanical Properties

  0.2% Proof Stress Tensile Strength Elongation Reduction of area Hardness
  MPA MPA % % HB
  Min Min Min  Min  
Sol treated and Aged
1800 Deg F (AMS 5732)
586 896 15 - 248 - 341
Sol Treated and Aged
1650 Deg F (AMS 5737)
655 965 12 - 277 - 363